Fiver beat me to it. That is the situation I'm in............too much pure, on hand. So I purchase lino, from Roto Metals, and mix accordingly.3 parts lead to 1 lino will give you 1% tin and 3% antimony.
that's about as close to WW alloy as you'll find.
Same here... but I use superhard, bottom line I am in same scenario, I have soft just need "need" hard.Fiver beat me to it. That is the situation I'm in............too much pure, on hand. So I purchase lino, from Roto Metals, and mix accordingly.