burbank.jung
Active Member
Currently, I heat up my pot where the Lee knob is just past halfway between off and high, drop my lead ingots in, and as soon as the lead is melted and my mold is heated, I start casting. Cast bullet keepers begin when my bullets don't have flaws. Maybe I should insert my thermometer to take a temperature reading and the lead happens to be the same temperature every time. I've read that you should turn your pot down untill you notice solidification and then turn the temperature up 100 degrees. What is your technique?